(E335+S) - Nr.(1.0060) (E335GC) - Nr.(1.0543)

Sulfur-Alloyed Carbon Steel for Machining

Carbon steel derived from the E335 type of the standard EN 10025-2; the addition of sulfur confers greater machinability by chip removal. Not suitable for hardening heat treatments.

References and Comparable Standards

Standard Reference: EN 10025-2: 2004 (Hot-rolled products) | EN 10277-2: 2008 (Bright products)

EUROPE		ITALY	GERMANY		FRANCE	UK	USA
EN 10025-2: 2004 EN 10277-2: 2008		(UNI 7070 - 72)	(DIN 17100-80)		(NF A 35-501-83)	(BS 4360 - 90)	ASTM A 29
Grade	N°		Werkstoff	N°
(E335+S)	(1.0060)	(Fe590+S)	(St60-2+S)	(1.0060)	(A60-2+S)	-	-
(E335GC)	(1.0543)	(Fe590+S)	(St60-2+S)	(1.0060)	(A60-2+S)	-	-

Chemical Composition (Cast Analysis) (%)

C	Si/max	Mn/max	P/max	S	N/max
0,37÷0,45	0,50	1,40	0,045	0,080÷0,120	0,011

Mechanical Properties - As Rolled Condition

Size (mm)	Rp0,2 (MPa) min	Rm (MPa) min	A5 (%) min
d≤16	335	570÷710	16
16<d≤40	325	570÷710	16
40<d≤63	315	570÷710	15
63<d≤80	305	570÷710	14
80<d≤100	295	570÷710	14
100<d≤150	275	550÷710	12
150<d≤200	265	540÷710	11
200<d≤230	255	540÷710	11

Mechanical Properties – Bright Steel

Size (mm)	as Rolled + Turned (+SH)		Cold Drawn (+C)
Size (mm)	Hardness HB	Rm (MPa)	Rp0,2 (MPa) min	Rm (MPa)	A5 (%) min
5≤d≤10	-	-	540	700÷1050	5
10<d≤16	-	-	480	680÷970	6
16<d≤40	169÷211	570÷710	390	640÷930	7
40<d≤63	169÷211	570÷710	340	620÷870	8
63<d≤100	169÷211	570÷710	295	570÷810	8

Working Temperatures Recommended

Operation	°C
Hot forgings deformation	900÷1150
Soft annealing	650÷700